PA66 Series (Polyamide, Nylon) Modified Engineering Plastic

PA66 Series (Polyamide, Nylon) Modified Engineering Plastic ISO9001:2008 Certified Factory

PHYSICAL PROPERTIES	Test method	Unit	A1G15	A1G30	A1G35	A1G50	A2Z	A8Z	A5ZBK	A5G25BK	A1MG30	A1M30
Water Absorb (24hr,23°C)	ISO 62	%	2.2	1.7	1.4	1.2	1.1	2.3	2.1	1.4	1.37	1.35
Density	ISO 1183	g/cm3	1.24	1.36	1.4	1.56	1.11	1.06	1.17	1.35	1.37	1.37
Ashy	ISO 1172	%	15	30	35	35	——	——	——	25	30	30
MECHANICAL PROPERTIES
Tensile strength	ISO 527	MPa	120	175	190	230	70	50	75	140	120	75
Elongation,at break	ISO 527	%	——	——	——	——	40	45	——	——	——	——
Flexural Stress	ISO 178	MPa	180	240	280	330	85	65	100	200	180	120
Flexural Modulus	ISO 178	MPa	5000	8000	9000	14000	2500	2000	3500	6500	6800	5600
Izod notched impact strength	ISO 180	KJ/m2	7.5	13	15	16	10	90	3	10	10	5
Charpy unnotched impact strength	ISO179	KJ/m2	45	70	75	90	NB	NB	25	60	55	40
Hardness,Rockwell	ISO 2039-2	R	120	120	120	120	115	100	115	120	115	115
THERMAL PROPERTIES
Heat Deflection Temperature 0.45MPa	ISO 75	°C	250	250	250	250	190	185	200	250	250	250
Heat Deflection Temperature1.82MPa	ISO 75	°C	240	240	240	240	80	60	65	240	240	240
Flame retardant	UL 94	Class	HB	HB	HB	HB	HB	HB	V0	HB	HB	HB
Melting point	ISO 3146	°C	258	258	260	260	258	258	258	258	258	258
Processing performance
Injection Molding Temperature		°C	250-290°C	250-290°C	250-290°C	250-290°C	260-300°C	260-300°C	250-280°C	250-280°C	250-290°C	250-290°C
Drying Temperature/Time		°C/h	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4
Linear Molding Shinkage		%	0.4-0.9	0.2-0.6	0.2-0.5	0.2-0.45	1.2-1.8	1.4-2.0	1.0-1.4	0.3-0.7	0.3-0.7	0.6-1.0

PA66 Series (Polyamide, Nylon) Modified Engineering Plastic