PA6 Series (Polyamide, Nylon) Modified Engineering Plastic

PA6 Series (Polyamide, Nylon) Modified Engineering Plastic ISO9001:2008 Certified Factory

PA6 Series (Polyamide, Nylon) Modified Engineering Plastic

PHYSICAL PROPERTIES	Test method	Unit	B1G15	B1G30	B1G45	B2Z	B8Z	B1MG40
Water Absorb (24hr,23°C)	ISO 62	%	2.6	2.1	0.8	2.5	1.1	1.37
Density	ISO 1183	g/cm3	1.24	1.36	1.51	1.1	1.06	1.37
Ashy	ISO 1172	%	15	30	45	——	——	30
Mechanic performance
Tensile strength	ISO 527	MPa	120	170	190	65	45	110
Elongation,at break	ISO 527	%	——	——	——	40	40	——
Flexural Stress	ISO 178	MPa	180	230	270	80	65	160
Flexural Modulus	ISO 178	MPa	5300	8000	12000	2200	1600	6500
Izod notched impact strength	ISO 180	KJ/m2	9	18	20	15	80	12
Charpy unnotched impact strength	ISO179	KJ/m2	50	85	90	NB	NB	55
Hardness,Rockwell	ISO 2039-2	R	120	120	120	110	110	115
THERMAL PROPERTIES
Heat Deflection Temperature 0.45MPa	ISO 75	°C	210	220	220	170	120	220
Heat Deflection Temperature1.82MPa	ISO 75	°C	180	200	210	70	55	210
Flammability	UL 94	Class	HB	HB	HB	V2	V2	HB
Melting point	ISO 3146	°C	220	220	220	220	220	220
ELECTRICAL PROPERTIES
Surface Surface	IEC167	Ω	10^13	10^13	10^13	10^13	10^13	10^13
Dielectric Strength	IEC 60243	KV/mm	20	21	22	18	18	22
PROCESSING
Injection Molding Temperature		°C	230—275°C	230—275°C	230—275°C	230—265°C	230—265°C	230—265°C
Mould Temperature		°C	60-90	60-90	60-90	60-80	60-80	60-90
Drying Temperature/Time		°C/h	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4	100-120/2-4
Linear Molding Shinkage		%	0.4-0.9	0.2-0.6	0.2-0.45	1.0-1.4	1.2-1.6	0.3-0.7

PA6 Series (Polyamide, Nylon) Modified Engineering Plastic